The powder of Y134, Y257 and Ti composite was synthesized by solid state reaction. The crystal structure of the powder was investigated by using powder X-ray diffraction. The raw data of XRD was characterized for phase separation of composition. The samples consist of a superconducting phase with orthorhombic structure and Pmmm space group and a non-superconducting phase that have various structures and space groups. The Ti doped affected the increasing c lattice parameters and superconducting phase. The impurity phase had no effect on increasing the c lattice superconducting phase. The c lattice parameters and superconducting phase was increased following the Ti-doped.
Keywords: Y134 superconductor, Y257 superconductor, titanium-doped
Corresponding author: Tel.: +66 851 09 0567 Fax: +66 77355 666
E-mail: kruaehong@hotmail.com
Kruaehong*, T. ., Sujinnapram, S. ., Udomsamuthirun, P. ., Nilkamjon, T. ., & Ratreng, S. . (2018). The Effect of Ti-doped on the Structure of Y134 and Y257 Superconductors. CURRENT APPLIED SCIENCE AND TECHNOLOGY, 126-132.